In order to improve immobilization process which is crucial for creating of high-performance biosensors, various techniques are used. In recent time, very often different types of nanoparticles become more popular for biosensor creation. One of these perspective nanomaterials is zeolite. Zeolites are hydrated microporous crystalline minerals. They are composed mainly of silicon, aluminum and oxygen. The modification of crystal structures makes it possible to obtain zeolites with different properties [1,2]. The regular microporous structure of the zeolite guarantees an improvement of the chemical and physical stabilities of the immobilized agent, whereas the porosity of the zeolite keeps open the access of the guest molecules or ions to the ambient. Furthermore, zeolites are able to exchange ions with some compounds. An important characteristic of zeolites is the Si/Al ratio. The increase of the Si/Al ratio results in higher thermal stability and hydrophobicity as in silicalite. Silicalite is one of the most studied zeolites that has both hydrophobic and organophilic selectivities. Also, silicalite has high thermal and chemical stabilities and high adsorption properties [3,4].
It has been previously reported on the development of biosensors based on zeolites for glucose determination [5,6]. Glucose oxidase was immobilized on the electrode surface modified with different types of zeolites by physical adsorption and by standard glutaraldehyde (GA) method. It has been found that biosensors based on zeolites had higher sensitivity comparing with others biosensors. Sensitivity and response time of developed biosensors depend on the amount of zeolite on the transducer’s surface .
Few modifications were reported on the immobilization procedure using silicalite and zeolite Beta for the conductometric urea biosensor creation . A natural zeolite clinoptilolite was also used for the same purpose . It was demonstrated that the characteristics of the conductometric urea biosensors based on urease adsorbed on silicalite are better than those of the biosensors based on urease immobilized only in GA vapor .
The usage of zeolites for fabrication of the biosensors for H2O2 detection based on cytochrome c  and the biosensor for DNA determination based on Ag/NaA zeolite-modified carbon paste electrode  were also considered, which appeared to be a very promising approach to further zeolites usage.
Therefore, the application of silicalite for the improvement of working characteristics of conductometric biosensors for sucrose determination was studied in this research.
The following enzymes and reagents were used: mutarotase (MUT) (ЕС 220.127.116.11) from pig’s kidney with activity of 100 U/mg from Biozyme Laboratories Ltd. (Blaenavon, UK); glucose oxidase (GOx) from Penicillium vitale (ЕС 18.104.22.168) with activity of 130 U/mg from Diagnosticum (L’viv, Ukraine); invertase (INV) (ЕС 22.214.171.124) from baker’s yeast with activity of 355 U/mg from Fluka AG - Chemische Fabrik (St. Galen, Switzerland); bovine serum albumin (BSA) (V fraction) from Sigma-Aldrich Chemie GmbH (Schnelldorf, Germany); 50% aqueous solution of GA, Sigma-Aldrich Chemie GmbH (Schnelldorf, Germany); glucose, maltose, lactose, and sucrose were from Sigma-Aldrich Chemie GmbH (Schnelldorf, Germany). Other non-organic compounds were of analytical grade.
The conductometric transducers were 5 × 30 mm2 in size and consisted of two identical pairs of stainless steel interdigitated electrodes deposited onto a ceramic support. The usage of two electrode pairs enabled differential mode of measurements.
The sensitive area of each electrode pair was about 1.5 × 2 mm2. The digits as well as interdigital spaces were 50 μm wide each. The image of stainless steel interdigitated electrodes obtained by scanning electron microscopy and the overall view of the conductometric transducer are presented in Figure 1.
Synthesis and characterization of silicalite
Silicalite was synthesized in the Middle East Technical University (Ankara, Turkey). The optimized molar composition of the solution used for synthesis of silicalite-1 is 1TPAOH:4TEOS:350H2O. Tetraethylorthosilicate (TEOS, 95%) was used as the silica source. Tetrapropylammonium hydroxide (TPAOH, 25%) was used as a template. By hydrolyzing tetraethoxysilane (TEOS) with tetrapropylammonium hydroxide (TPAOH) solution, a clear homogeneous solution was obtained at room temperature for 6 h under stirring. Afterwards, the resulting solution was placed in oven for 18 h at 125°C. Then to remove the unreacted material, the crystallized solid particles were centrifuged at 13,000 rpm, washed with deionized water, and dried at 80°C. The SEM (scanning electron microscope) image of synthesized silicalite depicted in Figure 2 shows that the prepared silicalite particles have size about 400 to 500 nm. X-ray diffraction (XRD) spectrum of silicalite is shown in Figure 3.
Creation of PEI silicalite-modified electrode
For preparing of biosensors based on PEI silicalite-modified electrodes, the electrode surfaces were dip-coated with mucasol for 15 min, rinsed with copious amount of distilled water, and dried under air. For formation of homogeneous layers of PEI, both drop coating and spin coating techniques have been tried since spin coating gave more homogeneous layers, it was continued to be used. In our study, polyethylenimine (PEI) was used as a layer between electrode surface and silicalite. The suitable conditions for silicalite monolayer production were chosen as spin coating with 0.5% PEI in ethanol at 3,000 rpm with 15 s and 100°C for calcination temperature during 30 min. This kind of PEI silicalite-modified electrode was used as a base for the preparation of polyethylenimine/silicalite (PEI/Sil) and polyethylenimine/glutaraldehyde/silicalite (PEI/GA/Sil) biosensors.
Creation of silicalite-modified electrode
A silicalite layer on the transducer surface was formed using drop-coating technique. We used 10% (w/w) silicalite solution in 5 mM phosphate buffer, pH 6.5. A constant amount of silicalite solution (0.2 ml) was deposited onto the active zone of each pair of electrodes, and then the transducer was heated for 2 min at 200°C. This temperature had no effect on the transducer working parameters. The procedure resulted in the formation of silicalite layer in the electrodes active zones. This kind of silicalite-modified electrode was used as a base for the preparation of Sil and GA/Sil biosensors.
Creation of biomembrane
To create an active membrane of sucrose biosensors, 20 mM phosphate buffer solution at pH 7.0 which contains 5% (w/w) of GOx, 5% (w/w) of MUT, 5% (w/w) of INV, and 5% (w/w) of BSA was mixed in 1:1 ratio with 2% (w/w) aqueous solution of GA for the immobilization on the surface of bare or silicalite-modified electrodes.
In order to obtain an active membrane of glucose biosensors, 20 mM phosphate buffer solution at pH 7.0 which contains 10% (w/w) of GOx and 5% (w/w) of BSA was mixed in 1:1 ratio with 2% (w/w) aqueous solution of GA in the same way as described above.
The mixture for reference membrane was prepared in analogous manner, except that the enzymes were replaced with BSA. Thus, the reference solution for sucrose biosensor contained 20% (w/w) BSA totally and 15% (w/w) BSA in the case of glucose biosensor. Enzyme and reference solutions were separately mixed with 2% (w/w) aqueous solution of GA in a ratio of 1:1. Immediately afterwards, we deposited the mixture of enzyme solution with GA on one pair of electrodes and the mixture of reference solution with GA was placed on another one. The time of immobilization was 15 min; GA formed strong covalent bonds between the compounds of bioselective membrane, whereas the whole bioselective membrane was attached to the electrode surface through weak (i.e., Van der Waals) bonds. After immobilization, the electrodes were submerged in the working buffer for 15 min to wash out the unbound enzyme and GA excess.
An example of following the procedure of creation of PEI/GA/Sil biosensor is shown in Figure 4.
Electrochemical measuring system
A portable conductometric analyzer was used to determine changes in conductivity in the near-electrode layer. The portative measuring device (9.5 cm × 2.5 cm × 13.5 cm) was produced in the Institute of Electrodynamics of National Academy of Sciences of Ukraine (Kiev, Ukraine). The applied sinusoidal potential with frequency of 36.5 kHz and amplitude of 14 mV allowed avoiding such effects as Faraday processes, double-layer charging, and polarization of the microelectrodes. Illumination and temperature variations had practically no influence on the biosensor characteristics. The measurements were carried out in a glass cell filled with phosphate buffer (volume 1 ml), under vigorous magnetic stirring.
The conductometric determination of sucrose and glucose, using the prepared biosensors, was realized in a differential measuring mode, which ensured satisfactory detection accuracy and suppression of non-informative effects of the environment (variations of temperature, рН, and background conductivity of working solution).
Measurements were carried out at room temperature in 5 mM phosphate buffer solution, pH 6.5, continuously stirred in an open 1 ml cell. The substrate concentrations in the cell were varied by the addition of the different volumes of the stock solution. All experiments were repeated in triplicate. The data in the figures were expressed either as a mean of three repeated results of experiment or as a mean ± standard deviation (SD). The experiments were performed at least in three series.
Results and discussion
The cascades of enzymatic reactions for sucrose detection by conductometric biosensor are presented below:
Three enzymes are used for measurement of sucrose while only one, glucose oxidase - for glucose. The enzyme invertase decomposes sucrose into β-D-fructose and α-D-glucose, which is transformed into β-D-glucose by mutarotase. β-D-glucose is decomposed by GOD to hydrogen peroxide and D-glucolactone. In its turn, D-glucolactone is spontaneously hydrolyzed to gluconic acid, which dissociates to the acid residue and a proton. These reactions lead to changes in solution conductivity what can be registered by a conductometric transducer.
First of all, we check the sensitivity of five types of biosensors based on different types of enzyme immobilization: (1) biosensors with GA without silicalite, (2) PEI silicalite-modified biosensors without immobilization in GA (PEI/Sil biosensor), (3) PEI silicalite-modified biosensors with immobilization in GA (PEI/GA/Sil biosensor), (4) silicalite-modified biosensors without immobilization in GA (Sil biosensor), and (5) silicalite-modified biosensor with immobilization in GA (GA/Sil biosensor) (Table 1). The PEI/GA/Sil biosensors are characterized by much higher sensitivity than the biosensors without GA and biosensors based only on GA cross-linking.
Thus, the method of enzyme immobilization with GA on PEI silicalite-modified electrodes was chosen as the most appropriate for the further biosensor fabrication; for this reason, the next study was carried out using only PEI/GA/Sil biosensors.
First of all, we studied the selectivity of PEI/GA/Sil sucrose biosensors. Biosensor selectivity, one of important analytical characteristics, depends on choice of both biological recognition element and transducer. An influence of interfering components (some carbohydrates) on response value was studied to test biosensor selectivity. For that purpose, glucose, maltose, sucrose, lactose, fructose, arabinose and galactose in concentration of 0.5 mM were added to a working cell (Figure 5).
In general, conductometric biosensors appeared to be sufficiently selective. There was no significant influence of common carbohydrates except of sucrose and glucose, which is expected. The sucrose biosensors are highly sensitive not only to sucrose but also to glucose because the enzyme membrane of sucrose biosensors contains also glucose oxidase. For this reason, to determine sucrose in multicomponent solution, we used two biosensors: sucrose biosensor that gives the summary response to both substrate (sucrose and glucose) and glucose biosensor that selectively determines only glucose.
Reproducibility is one of the most important working characteristics of biosensors. To determine signal reproducibility, the biosensors’ responses to 0.25 mM glucose and sucrose were measured during one working day with 10- to 15-min intervals. The biosensors were kept in the continuously stirred buffer solution at room temperature during intervals between measurements. As seen from Figure 6, the biosensor responses were highly reproducible. The relative standard deviation (RSD) for glucose measurements was 2.78% and for sucrose measurements was 3.2% which is quite acceptable value (Figure 6).
The calibration curves to glucose and sucrose by PEI/GA/Sil sucrose biosensor are shown on Figure 7. The PEI/GA/Sil sucrose biosensors showed extended linear range of sucrose detection comparing with traditional type of biosensors based on immobilization in GA without silicalite. The linear range of PEI/GA/Sil sucrose biosensors was 0.0035 to 4 mM for sucrose and 0.0015 to 1.75 mM for glucose (Figure 7). The limit of detection (LOD) for glucose determination was 1.5 μM and LOD for sucrose determination was 3.5 μM.
We used PEI/GA/Sil biosensors for the determination of sucrose concentration in different sweet beverages. Obtained results were compared with results of high-performance liquid chromatography (HPLC) (Table 2). The correlation between the methods is high (R = 0.99).
It was concluded that the method of enzyme adsorption on PEI silicalite-modified electrodes with GA is well suited for the biosensor manufacture.
Conductometric enzyme biosensors based on different type of silicalite-modified electrodes were created and compared. PEI/GA/Sil biosensors have shown higher sensitivity to substrate compared with others biosensors tested in this work. Moreover, the PEI/GA/Sil sucrose biosensors were characterized by high selectivity and signal reproducibility (RSD = 2.78% for glucose measurements and RSD = 3.2% for sucrose measurements). PEI/GA/Sil sucrose biosensors were used to determine the concentrations of sucrose in different beverage samples. The results of biosensor measurements of sucrose in beverages had a high correlation (R = 0.99) with the results obtained by HPLC. Thus, the method of enzyme immobilization using PEI/GA/Sil composition is highly effective and perspective for biosensor creation.
high-performance liquid chromatography
limit of detection
relative standard deviation
Competing interests The authors declare that they have no competing interests.
Authors’ contributions PVN and OYD performed enzyme immobilization on silicalite-modified conductometric electrodes and studied analytical characteristics of developed enzyme biosensors. BOK synthesized silicalite and deposited silicalite on the surface of the conductometric transducers. BAK planned the experiments, controlled the zeolites synthesis by electron microscopy, made XRD spectrum of silicalite. OYD, PVN, and OOS processed the results, wrote, and arranged the article. SVD and FL proposed an idea of the development of conductometric enzyme biosensors based on silicalite-modified electrodes. SVD and FL are supervisors of the whole work, the results of which are presented in this research. All authors read and approved the final manuscript.
The authors gratefully acknowledge the financial support of this study by Project European IRSES-NANODEV. Furthermore, this study was partly supported by National Academy of Sciences of Ukraine in the frame of complex scientific-technical program ‘Sensor devices for medical-ecological and industrial purposes: metrology and trial performance.’
Mintova, S; Gilson, JP; Valtchev, V: Advances in nanosized zeolites, Roy Soc Ch, 2013, 5, S. 6693–703
Valdes, MG; Perez-Cordoves, AI; Diaz-Garcia, ME: Zeolites and zeolite-based materials in analytical chemistry, Trend Anal Chem, 2006, 25, S. 24–30Crossref
Ju, H: Bioanalysis based on nanoporous materials, Trend Anal Chem, 2012, 39, S. 149–62Crossref
Muresan, LM: Zeolite-modified electrodes, Pure Appl Chem, 2011, 83, S. 325–43
Goriushkina, T; Kurç, BA; Sacco, A; Dzyadevych, SV: Application of zeolites for immobilization of glucose oxidase in amperometric biosensors, Sens Electron and Microsyst Technol, 2010, 1, S. 36–42
Soldatkin, OO; Kucherenko, IS; Shelyakina, MK; Soy, E; Kirdeciler, K; Öztürk, S: Elaboration of new method of enzyme adsorption on silicalite and nano beta zeolite for amperometric biosensor creation, Biopolym Cell, 2014, 30, S. 291–8Crossref
Saiapina, OY; Pyeshkova, VM; Soldatkin, OO; Melnik, VG; Kurç, BA; Walcarius, A: Conductometric enzyme biosensors based on natural zeolite clinoptilolite for urea determination, Mat Sci Eng, 2011, 31, S. 1490–7Crossref
Kucherenko, IS; Soldatkin, OO; Kasap, BO; Öztürk, S; Akata Kurc, B; Soldatkin, AP: Elaboration of urease adsorption on silicalite for biosensor creation, Electroanal, 2012, 24, S. 1380–5Crossref
Dai, Z; Liu, S; Ju, H: Direct electron transfer of cytochrome c immobilized on a NaY zeolite matrix and its application in biosensing, Electrochim Acta, 2004, 49, S. 2139–44Crossref
Azizi, SN; Ranjbar, S; Raoof, JB; Hamidi-Asl, E: Preparation of Ag/NaA zeolite modified carbon paste electrode as a DNA biosensor, Sensor Actuator, 2013, 181, S. 319–25Crossref